| 棱角钢砂 |
棱角钢砂 |
|
|
1、钢砂粒度分布图：
棱角钢砂颗粒度
|
| 产品直径(mm) |
相应筛网上累积残留率% |
| G10 2mm |
|
通过 |
|
80%
min |
90%
min |
|
|
|
|
|
|
|
|
|
|
|
|
| G12 1.7mm |
|
|
通过 |
|
80%
min |
90%
min |
|
|
|
|
|
|
|
|
|
|
|
| G14 1.4mm |
|
|
|
通过 |
|
80%
min |
90%
min |
|
|
|
|
|
|
|
|
|
|
| G16 1.2mm |
|
|
|
|
通过 |
|
75%
min |
85%
min |
|
|
|
|
|
|
|
|
|
| G18 1mm |
|
|
|
|
|
通过 |
|
75%
min |
|
85%
min |
|
|
|
|
|
|
|
| G25 0.7mm |
|
|
|
|
|
|
通过 |
|
|
70%
min |
|
|
80%
min |
|
|
|
|
| G40 0.4mm |
|
|
|
|
|
|
|
通过 |
|
|
|
|
70%
min |
|
80%
min |
|
|
| G50 0.3mm |
|
|
|
|
|
|
|
|
|
通过 |
|
|
|
|
65%
min |
75%
min |
|
| G80 0.2mm |
|
|
|
|
|
|
|
|
|
|
|
|
通过 |
|
|
65%
min |
75%
min |
| SAE 筛网号 |
6 |
7 |
8 |
10 |
12 |
14 |
16 |
18 |
20 |
25 |
30 |
35 |
40 |
45 |
50 |
80 |
120 |
| 筛网孔径 (mm) |
3.35 |
2.80 |
2.36 |
2.00 |
1.70 |
1.40 |
1.18 |
1.00 |
0.85 |
0.71 |
0.60 |
0.50 |
0.425 |
0.335 |
0.30 0 |
0.18 0
|
0.125 |
2、钢砂性能简介
|
优质合金钢砂，密度高、缺陷少，金相组织良好，机械性能优越，具有良好的韧性和抗破碎、抗疲劳性能，复用率高
消耗低。棱角状钢砂由于具有多棱角的形状，在喷砂过程中大大提高对金属表面的清理能力。 |
Ａ组：硬度>60HRC
此类钢砂为切割花岗岩石用钢砂，具有：性能稳定、粒度均匀、耐磨性好等特点，经众多石材厂家多年使用证明，比
国外生产的圆弧砂更锋利、锯切石材速度更快、石材锯切板面更平整。 |
Ｂ组：硬度>40-52HRC
新制成时是棱角状的，使用过程中逐渐被磨圆，特别适合于去除氧化皮及表面清理作业。
|
Ｃ组 : 硬度>53-60HRC
比B组钢砂硬度更高，喷砂过程中棱角及会慢慢失去，特别适合于去 除氧化皮及表面清理，预处理作业。
|
3、钢砂主要特性分布表：
钢砂主要特性 |
| 项目 |
钢砂 |
| 形状 |
棱角状 |
| 化学成分% |
C |
Si |
Mn |
S |
P |
其它
合金元素 |
| 0.85-1.20 |
0.61-1.20 |
0.6-1.20 |
<0.05 |
<0.05 |
适量 |
硬度日本
HVK-HO型显微
硬度计测定 |
A 组
>60HRC
(>710HV) |
B 组
40-52HRC
(377-540HV) |
C 组
53-60HRC
(570-710HV)
|
| 金相组织( × 400) |
细匀
回火马氏体 |
细匀
回火 屈 氏体 |
细匀
回火马氏体 |
碳化物级别<2
|
| 醇比重测定密度 |
≥7.50g/cm3 |
4、包装：
1. 复合袋包装(内套塑料袋)，净重：25kg/袋。
2. 木架托盘包装，净重：1000kg/托盘。 |
|
|
|
|
磨具